LaNi4.25Al0.75吸氕、氘、氚热力学同位素效应

doi:10.7538/tws.2016.29.02.0089

摘要/Abstract

摘要：

采用自制的全金属氢化物吸放氢实验装置，恒温等容条件下测定LaNi_4.25Al_0.75材料吸氕、氘、氚单质气体的压力-组成等温线（P-C-T曲线），并根据Van’t Hoff(范特霍夫）方程得到LaNi_4.25Al_0.75吸氕、氘、氚形成氢化物相的热力学参数焓变ΔH分别为：-44.5、-45.0、-47.1 kJ•mol^-1，熵变ΔS分别为：-118.0、-121.8、-127.5 J•mol^-1•K^-1。结果表明：LaNi_4.25Al_0.75材料吸收氕、氘、氚单质气体，在温度较低时，同位素效应不明显；温度高于100℃时，热力学同位素效应显著。相同温度、吸气容量条件下，吸气平衡压力从低到高依次是氕、氘和氚，其反应焓变和熵变从小到大依次是氚、氘和氕。结果表明，LaNiAl合金吸氢的热力学同位素效应依赖于温度的变化。

关键词: LaNi_4.25Al_0.75, 同位素效应, 热力学, 储氢材料

Abstract:

The P-C-T curves of LaNi_4.25Al_0.75 alloy absorbing protium, deuterium and tritium were investigated at constant temperature and volume in our metal hydride research system. According to the Van’t Hoff Equation, the thermodynamics parameters of the hydride phase were determined. Enthalpy change and entropy change for protium, deuterium and tritium were -44.5, -45.0, -47.1 kJ/mol and -118.0, -121.8, -127.5 J•mol^-1•K^-1. The experiments indicated that the isotope effect did not obviously at low temperature, however, as the temperature increasing to 100 ℃, there were obvious thermodynamics isotope effect with hydrogen absorption by LaNi_4.25Al_0.75 alloy. The order of equilibrium pressure absorbing gases was T₂>D₂>H₂. However, the enthalpy and entropy appeared to be in verse order, T₂>D₂>H₂. The results showed that hydrogen isotope effect with LaNiAl alloys were depended on temperature.

Key words: LaNi_4.25Al_0.75, isotope effect, thermodynamics, hydrogen storage materials

梁斌斌;赵崴巍;何长水;阙骥;杨洪广. LaNi_4.25Al_0.75吸氕、氘、氚热力学同位素效应[J]. 同位素, 2016, 29(2): 89-92.

LIANG Bin-bin;ZHAO Wei-wei;HE Chang-shui;QUE Ji;YANG Hong-guang. Thermodynamics Isotope Effects of LaNi_4.25Al_0.75 Absorbing Protium,Deuterium and Tritium[J]. Journal of Isotopes, 2016, 29(2): 89-92.

参考文献

［1］Vucht J H N V, Kuijpers F A, Bruning H C A M. Reversible room-temperature absorption of large quantities of hydrogen by intermetallic compounds［J］. Philips Research Reports, 1969, 25(2): 133-138.
［2］Thiébaut S, Douilly M, Contreras S, et al. He-3 retention in LaNi₅ and Pd tritides: Dependence on stoichiometry, He-3 distribution and aging effects［J］. Journal of Alloy and Compounds, 2007, 446(446): 660-669.
［3］Wermer J R. Analysis of LaNi_4.25Al_0.75 (LANA.75) tritide after five years of tritium exposure［R］. South Carolina:Westinghouse Savannah River Company, 1993.
［4］Heung L K. Design of metal hydrid vessels for processing tritium, WSRC-MS-2001-00179［R］. South Carolina: Westinghouse Sanannah River Company, 2001.
［5］Shanahan K L. ³He recovery from a Tritium-aged LANA75 sample, SRNL-STI-2010-00451［R］. South Carolina: Westinghouse Sanannah Rive National Laboratory, Aiken, 2010.
［6］Mohan G, Maiya M P, Murthy S S. Performance simulation of metal hydride hydrogen storage device with embedded filters and heat exchanger tubes［J］.International Journal of Hydrogen Energy, 2007, 32(18): 4978-4987.
［7］Goodell P D. Stability of rechargeable hydriding alloys during extended cycling［J］. Journal of the Less Common Metals, 1984, 99(1): 1-14.
［8］Ortman M S, Heung L K, Nobile A, et al. Tritium processing at the Savannah River site［J］. Fusion Technology, 1990, 21(2): 594-598.
［9］Mendelsohn M H, Gruen D M, Dwight A E. LaNi5-xAl is a wersatile alloy system for metal hydride applicatioin［J］. Nature, 1977, 269(5 623): 45-47.
［10］Diaz H, Percheron-Gukgan A, Achard J C, et al. Thermodynamics and structural properties of LaNi_5-yAl_ycompounds and their related hydrides［J］. International Journal of Hydrogen Energy, 1979, 4(5): 445-454.
［11］胡子龙. 贮氕材料［M］. 北京：化学工业出版社，2002：68-69.
［12］Sicking G H. Isotope effects in metal—hydrogen systems［J］. Journal of the Less Common Metals, 1984, 101(8): 169-l90.
［13］钱存富，杜昊，王洪祥. LaNi₅型储氢材料最大储氢量的讨论［J］. 稀有金属材料与工程,2000,29（1）：25-27.Qian Cunfu,Du Hao,Wang Hongxiang. Maximum hydrogen-storage capacity of LaNi₅ type hydrogen storage materials［J］. Raremetal Materimals and Engineering, 2000, 29(1): 25-27(in Chinese).
［14］Walters R T .Comment on “Tritium absorption-desorption characteristics of LaNi_4.25Al_0.75”［J］. Journal of Alloys & Compounds, 2008, 464(1): 10-12.
［15］Wang W D, Long X G, Cheng G J, et al. Tritium absorption-desorption characteristics of LaNi_4.25Al_0.75［J］. Journal of Alloys & Compounds, 2007, 441(441): 359-363.

[1]	韩磊;马福秋;薛云;矫彩山. 偕胺肟聚丙烯腈对铀酰离子吸附热力学及动力学过程分析[J]. 同位素, 2019, 32(1): 13-21.
[2]	王保柱 ;张东 ;石正坤 ;吴涛 . 钛硅酸钠（Na₂Ti₂O₃SiO₄·2H₂O）对Cs的吸附热力学分析[J]. 同位素, 2012, 25(1): 42-46.
[3]	刘杰超;马永健;窦亮. ¹²C¹⁸O和¹³C¹⁶O分子Ｘ¹Σ⁺基态的完全振动能谱和同位素位移[J]. 同位素, 2011, 24(1): 24-28.
[4]	王伟伟;龙兴贵;刘文科;黄刚. Mo含量对Ti-Mo合金氢同位素效应的影响[J]. 同位素, 2009, 22(3): 156-159.
[5]	王伟伟;龙兴贵;黄刚. Ti-Mo合金氢化物放氢动力学同位素效应研究[J]. 同位素, 2008, 21(4): 193-.
[6]	作者. 钛吸氕、氘和氚的热力学同位素效应[J]. 同位素, 2004, 17 (4 ): 218-218 .
[7]	作者. 模拟分析体内外~(153)Sm-EDTMP热力学平衡组分 [J]. 同位素, 2003, 16(Z1 ): 165-165 .
[8]	作者. 天然光卤石(KMgCl_3·6H_2O)中结晶水的氧同位素效应研究 [J]. 同位素, 1995, 8 (3 ): 129-132 .
[9]	作者. 冠醚萃取体系中锂的同位素效应──混合锂盐效应 [J]. 同位素, 1994, 7 (3 ): 168-171 .
[10]	作者. 多醚萃取体系中锂的同位素效应——盐浓效应 [J]. 同位素, 1991, 4 (3 ): 166-166 .